Ripe carambolas are hard to store and transport, while freeze-dried ones are easy to store. However, its long production time leads to higher costs. This study shows that high hydrostatic pressure (HHP) treatment could shorten the freeze-drying time of carambola slices. After HHP treatment (25–250 MPa), the drying time of the fresh sample can be shortened by 33.3–44.4% and the distribution of water and pigment in tissues is much uniform. With the increment of the pressure, 2,2-diphenyl-1-picrylhydrazyl (DPPH) and hydroxyl radical scavenging rate are increased. At 250 MPa, the total phenolic content (TPC) increased from 11.34 to 13.36 mg GAE g⁻¹, and the total flavonoid content (TFC) of the control sample was increased from 10.77 to 12.73 mg RE g⁻¹. Compared with the untreated sample, HHP treatment can enhance the flavour and shorten the freeze-drying time. This work guides the application of HHP technology for drying food processing.     

B4C–TiB2 composites fabricated by hot pressing TiC–B mixtures: The effect of B excess

Previous research have reported that B₄C–TiB₂ composites could be prepared by the reactive sintering of TiC–B powder mixtures. However, due to spontaneous oxidation of raw powders, using TiC–B powder mixtures with a B/TiC molar ratio of 6: 1 introduced an intermediate phase of C during the sintering process, which deteriorated the hardness of the composites. In this report, the effects of B excess on the phase composition, microstructure, and mechanical properties of B₄C–TiB₂ composites fabricated by reactive hot pressing TiC–B powder mixtures were investigated. XRD and Raman spectra confirmed that lattice expansion occurred in B-rich boron carbide and B_xC–TiB₂ (x > 4) composites were obtained. The increasing B content improved the hardness and fracture toughness but decreased the flexural strength of B_xC–TiB₂ (x > 4) composites. When the molar ratio of B/TiC increased from 6.6:1 to 7.8:1, the Vickers hardness and the fracture toughness of the composites were enhanced from 26.7 GPa and 4.53 MPa m^1/2 to 30.4 GPa and 5.78 MPa m^1/2, respectively. The improved hardness was attributed to the microstructural improvement, while the toughening mechanism was crack deflection, crack bridging and crack branching.     

Fabrication of alumina ceramics with functional gradient structures by digital light processing 3D printing technology

Alumina ceramics with different unit numbers and gradient modes were prepared by digital light processing (DLP) 3D printing technology. The side length of each functional gradient structure was 10 mm, the porosity ratio was controlled to 70%, and the number of units were (1 × 1 × 1 unit) and (2 × 2 × 2 unit) respectively. The different gradient modes were named FCC, GFCC-1, GFCC-2 and GFCC-3. SEM, XRD, and other characterization methods proved that these gradient structures of alumina ceramics had only α-Al2O3 phase and good surface morphology. The mechanical properties and energy absorption properties of alumina ceramics with different functional gradient structures were studied by compression test. The results show that the gradient structure with 1 × 1 × 1 unit has better mechanical properties and energy absorption properties when the number of units is different. When the number of units is the same, GFCC-2 and GFCC-3 gradient structures have better compressive performance and energy absorption potential than FCC structures. The GFCC-2 gradient structure with 1 × 1 × 1 unit has a maximum compressive strength of 19.62 MPa and a maximum energy absorption value of 2.72 × 105 J/m3. The good performance of such functional gradient structures can provide new ideas for the design of lightweight and compressive energy absorption structures in the future.     

Engineering the hydrogen storage properties of the perovskite hydride ZrNiH3 by uniaxial/biaxial strain

In the present work, the bonding length, electronic structure, stability, and dehydrogenation properties of the Perovskite-type ZrNiH₃ hydride, under different uniaxial/biaxial strains are investigated through ab-initio calculations based on the plane-wave pseudo-potential (PW-PP) approach. The findings reveal that the uniaxial/biaxial compressive and tensile strains are responsible for the structural deformation of the ZrNiH₃ crystal structure, and its lattice deformation becomes more significant with decreasing or increasing the strain magnitude. Due to the strain energy contribution, the uniaxial/biaxial strain not only lowers the stability of ZrNiH₃ but also decreases considerably the dehydrogenation enthalpy and decomposition temperature. Precisely, the formation enthalpy and decomposition temperature are reduced from ?67.73 kJ/mol.H₂ and 521 K for non-strained ZrNiH₃ up to ?33.73 kJ/mol.H₂ and 259.5 K under maximal biaxial compression strain of ε = ?6%, and to ?50.99 kJ/mol.H₂ and 392.23 K for the maximal biaxial tensile strain of ε = +6%. The same phenomenon has been also observed for the uniaxial strain, where the formation enthalpy and decomposition temperature are both decreased to ?39.36 kJ/mol.H₂ and 302.78 K for a maximal uniaxial compressive strain of ε = - 12%, and to ?51.86 kJ/mol.H₂ and 399 K under the maximal uniaxial tensile strain of ε = +12%. Moreover, the densities of states analysis suggests that the strain-induced variation in the dehydrogenation and structural properties of ZrNiH₃ are strongly related to the Fermi level value of total densities of states. These ab-initio calculations demonstrate insightful novel approach into the development of Zr-based intermetallic hydrides for hydrogen storage practical applications.     

Polymorphism in Gd2Ge2O7 ceramics: Structural,vibrational, and optical features

In this work, Gd₂Ge₂O₇ polymorphs were obtained by solid-state reactions at 1100–1300 °C. Structural and vibrational features were investigated by X-ray diffraction and Raman spectroscopy. For the triclinic (space group P1) polymorph, all the predicted phonons were discerned in perfect agreement with the group theory calculations, while for the tetragonal polymorph (space group P4₁2₁2), 53 bands of the 81 predicted modes could be identified and characterized. The Gd³⁺ 4f-4f electronic transitions were investigated by diffuse reflectance spectroscopy in the range 200–340 nm. By applying the Kubelka-Munk function, it was possible to determine the bandgap values for all ceramics studied. The tetragonal polymorph exhibited higher bandgap values (5.88 eV) than the triclinic one (5.59 eV), which are both more energetic than other pyrochlore polymorphs reported in the literature. The results indicate that the presence of polymorphism in Gd₂Ge₂O₇ ceramics can be used to produce tailor-made materials since their crystal structures have a strong influence on their optical properties. Consequently, these properties could be used to tuning the optical properties of Gd-containing materials to sensitize and transfer energy to other luminescent lanthanide ions, aiming for innovative applications.     

Diluted chemical bath deposition of CdZnS as prospective buffer layer in CIGS solar cell

In this study, dilute chemical bath deposition technique has been used to deposit CdZnS thin films on soda-lime glass substrates. The structural, morphological, optoelectronic properties of as-grown films have been investigated as a function of different Zn²⁺ precursor concentrations. The X-ray diffractogram of CdS thin-film reveals a peak corresponding to (002) plane with wurtzite structure, and the peak shift has been observed with the increase of the Zn²⁺ concentration upon formation of CdZnS thin film. From morphological studies, it has been revealed that the diluted chemical bath deposition technique provides homogeneous distribution of film on the substrate even at a lower concentration of Zn²⁺. Optical characterization has shown that the transparency of the film is influenced by Zn²⁺ concentration and when the Zn²⁺ concentration is varied from 0 M to 0.0256 M, bandgap values of resulting films range from 2.42 eV to 3.90 eV while. Furthermore, electrical properties have shown that with increasing zinc concentration the resistivity of the film increases. Finally, numerical simulation validates and suggests that CdZnS buffer layer with composition of 0.0032 M Zn²⁺ concentration would be a promising candidate in CIGS solar cell.     

Facile fabrication of silk fibroin/graphene oxide composite films and real-time morphological observation in stretching

Layer-structured regenerated silk fibroin (SF)/graphene oxide (GO) composite films were fabricated by a facile solution casting method. Fourier transform infrared spectroscopy, X-ray diffraction, and thermal gravity analysis confirmed the successful incorporation and uniform dispersion of graphene oxides in the SF matrix. To visualize GO's effect on the morphological evolution, atomic force microscopic images were recorded in real-time during the composite elongation to establish a correlation between microscopic structural characters and macroscopic mechanical properties. The result showed that the incorporation of graphene oxide into the SF matrix resulted in chain conformational transition, film surface flattening, and mechanical reinforcement. Surface roughness dramatically decreased from 65 to 10 nm, while tensile modulus increased substantially from 8.61 to 22.37 MPa by adding well-dispersed graphene oxide up to 1 wt% into the SF matrix. Through the real-time AFM observation under the horizontal stretching mode, the surface topography of original SF films varied from tori-spherical aggregations to rod-like ones resulting from GO's incorporation. In the meantime, SF's hydrophobicity was also increased, as manifested by contact angle increase from 30.81° to 45.09°.     

Good dielectric performance and broadband dielectric polarization in Ag,Nb co-doped TiO2

Due to the demand of miniaturization and integration for ceramic capacitors in electronic components market, TiO₂-based ceramics with colossal permittivity has become a research hotspot in recent years. In this work, we report that Ag⁺/Nb⁵⁺ co-doped (Ag_1/4Nb_3/4)_xTi_1−xO₂ (ANTOx) ceramics with colossal permittivity over a wide frequency and temperature range were successfully prepared by a traditional solid–state method. Notably, compositions of ANTO0.005 and ANTO0.01 respectively exhibit both low dielectric loss (0.040 and 0.050 at 1 kHz), high dielectric permittivity (9.2 × 10³ and 1.6 × 10⁴ at 1 kHz), and good thermal stability, which satisfy the requirements for the temperature range of application of X9R and X8R ceramic capacitors, respectively. The origin of the dielectric behavior was attributed to five dielectric relaxation phenomena, i.e., localized carriers' hopping, electron–pinned defect–dipoles, interfacial polarization, and oxygen vacancies ionization and diffusion, as suggested by dielectric temperature spectra and valence state analysis via XPS; wherein, electron-pinned defect–dipoles and internal barrier layer capacitance are believed to be the main causes for the giant dielectric permittivity in ANTOx ceramics.     

Hydraulic reactivity and cement formation of baghdadite

In this study, the hydraulic reactivity and cement formation of baghdadite (Ca₃ZrSi₂O₉) was investigated. The material was synthesized by sintering a mixture of CaCO₃, SiO₂, and ZrO₂ and then mechanically activated using a planetary mill. This leads to a decrease in particle and crystallite size and a partial amorphization of baghdadite as shown by X-ray powder diffraction (XRD) and laser diffraction measurements. Baghdadite cements were formed by the addition of water at a powder to liquid ratio of 2.0 g/ml. Maximum compressive strengths were found to be ~2 MPa after 3-day setting for a 24-h ground material. Inductively coupled plasma mass spectrometry (ICP-MS) measurements showed an incongruent dissolution profile of set cements with a preferred dissolution of calcium and only marginal release of zirconium ions. Cement formation occurs under alkaline conditions, whereas the unground raw powder leads to a pH of 11.9 during setting, while prolonged grinding increased pH values to approximately 12.3.